Cladding welding of CA6M with pulsed FCAW and results analysis through the L9 TAGUCHI and ANOVA
Cita com:
hdl:2117/368123
Tipus de documentArticle
Data publicació2018
Condicions d'accésAccés obert
Llevat que s'hi indiqui el contrari, els
continguts d'aquesta obra estan subjectes a la llicència de Creative Commons
:
Reconeixement-NoComercial-SenseObraDerivada 4.0 Internacional
Abstract
The cladding welding analysis with pulsed flux cored arc welding (FCAW) process, were carried over a AISI 1020 base metal (thickness 12,7 mm, width 63,5 and length 185mm) with an CA6NM steel wire with diameter of 1.2mm. Was performed only one weld cord in the flat position. For experimental design was used the method of Taguchi L9 to determinate the parameter to be analyzed through the application of the analysis of variance (ANOVA) method. The response signals in RMS (Root Mean Square) analyzed were the voltage, current and acceleration. The procedure is based on a non-parametric domain-selective ANOVA for functional data, which results in the selection of the intervals of the domain presenting the most statistically significant effects of each factor over the selected response signals. The statistical results presented by ANOVA show that not all the selected variables have influenced the results. The best results for the cladding welding were obtained from the current average of230amperes, and statistically the average current was the variable that significantly affected the results, however, the welding speed only affected the yield of the process.
CitacióMoreno, J. [et al.]. Cladding welding of CA6M with pulsed FCAW and results analysis through the L9 TAGUCHI and ANOVA. "International Journal of Advanced Engineering Research and Science", 2018, vol. 5, núm. 5, p. 150-157.