Significantly improved dehydrogenation of ball-milled MgH2 doped with CoFe2O4 nanoparticles
Significantly improved...pdf (4,591Mb) (Restricted access) Request copy
Què és aquest botó?
Aquest botó permet demanar una còpia d'un document restringit a l'autor. Es mostra quan:
- Disposem del correu electrònic de l'autor
- El document té una mida inferior a 20 Mb
- Es tracta d'un document d'accés restringit per decisió de l'autor o d'un document d'accés restringit per política de l'editorial
Rights accessRestricted access - publisher's policy
CoFe2O4 nanoparticles are added to magnesium hydride (MgH2) by high-energy ball milling in order to improve its hydriding properties. The hydrogen storage properties and catalytic mechanism are investigated by pressure-composition-temperature (PCT), differential thermal analysis (DTA), X-ray diffraction (XRD), field-emission scanning electron microscopy (FESEM) and transmission electron microscopy (TEM). The nonisothermal desorption results show that the onset desorption temperature of the MgH2 + 7 mol% CoFe2O4 is 160 degrees C, which is 200 degrees C lower than of the as-received MgH2. The dehydrogenation process of the MgH2 doped with the CoFe2O4 nanoparticles includes two steps. DTA curves and XRD patterns reveal that a chemical reaction happens between MgH2 and CoFe2O4, forming the final products of the ternary combination, corresponding to Co3Fe7, MgO and Co. The onset desorption temperature of the ball-milled MgH2 doped with Co3Fe7, MgO and Co is about 260 degrees C, approximately 100 degrees C lower than the un-doped MgH2, demonstrating that the ternary combination (Co3Fe7, MgO, and Co) also has a great catalytic effect on the MgH2 hydrogen storage properties. It is also confirmed that the various methods of adding the ternary combination have different effects on the MgH2 hydriding-dehydriding process. (C) 2014 Elsevier B.V. All rights reserved.
CitationShan, J. [et al.]. Significantly improved dehydrogenation of ball-milled MgH2 doped with CoFe2O4 nanoparticles. "Journal of power sources", 05 Desembre 2014, vol. 268, p. 778-786.
|Significantly improved...pdf||4,591Mb||Restricted access|
All rights reserved. This work is protected by the corresponding intellectual and industrial property rights. Without prejudice to any existing legal exemptions, reproduction, distribution, public communication or transformation of this work are prohibited without permission of the copyright holder