Sheets of branched poly(lactic acid) obtained by one step reactive extrusion calendering process: Physical Aging and Fracture Behaviour
Cailloux, Jonathan; Santana Pérez, Orlando Onofre; Franco-Urquiza, Edgar; Bou, Jordi; Carrasco Alonso, Félix Ángel; Maspoch Rulduà, M. Lluïsa (Springer, 2014-03-13)
Article
Accés restringit per política de l'editorial -
Sheets of branched poly(lactic acid) obtained by one-step reactive extrusion-calendering process: physical aging and fracture behavior
Cailloux, Jonathan; Santana Pérez, Orlando Onofre; Franco Urquiza, Edgar Adrian; Bou Serra, Jordi; Carrasco Alonso, Félix Ángel; Maspoch Rulduà, M. Lluïsa (2014-06-01)
Article
Accés restringit per política de l'editorialThe architectural modifications of a linear poly(D,L-Lactide) acid (PD,L-LA) commercial grade were induced by a one-step reactive extrusion-calendering process using a styrene-glycidyl acrylate copolymer as reactive agent. ... -
Sheets of poly(lactide)/o-MMT prepared by one-step reactive extrusion-calendering process
Cailloux, Jonathan; Bin Raja-Nazri, Raja Nazrul Hakim; Santana Pérez, Orlando Onofre; Sánchez Soto, Miguel; Franco-Urquiza, Edgar; Carrasco Alonso, Félix Ángel; Maspoch Rulduà, M. Lluïsa (Universidad de Sevilla. Grupo de Elasticidad y Resistencia de Materiales, 2014)
Text en actes de congrés
Accés obertIn this study, a reactive extrusion-calendering process was used in order to manufacture OMMT-based (2.5 wt.%) PLA-REX sheets with a nominal thickness of 1 mm. During processing, the properties of the melt were stabilized ... -
Thermal degradation of poly(lactic acid) and acrylonitrile-butadiene-styrene bioblends: Elucidation of reaction mechanisms
Carrasco Alonso, Félix Ángel; Santana Pérez, Orlando Onofre; Cailloux, Jonathan; Sánchez Soto, Miguel; Maspoch Rulduà, M. Lluïsa (2017-05-15)
Article
Accés obertSquare plates (nominal tickness: 3 mm, nominal width: 100 mm) of diferent rheolgically modified PLA/acrylonitrile-butadiene-styrene (ABS) blends were manufactured through injection molding process. During processing, the ... -
Using viscoelastic properties to quantitatively estimate the amount of modified poly(Lactic Acid) chains through reactive extrusion
Cailloux, Jonathan; Santana Pérez, Orlando Onofre; Bou Serra, Jordi; Carrasco Alonso, Félix Ángel; Maspoch Rulduà, M. Lluïsa (2015-05-12)
Article
Accés obertIn this study the dynamic viscoelastic properties of three structurally modified poly(lactic acid) (PLA) samples processed through reactive extrusion were analyzed. While classical chromatographic and spectroscopic techniques ...