Show simple item record

dc.contributorAnglada Gomila, Marcos Juan
dc.contributor.authorPavón Palacio, Juan José
dc.contributor.otherUniversitat Politècnica de Catalunya. Departament de Ciència dels Materials i Enginyeria Metal·lúrgica
dc.date.accessioned2011-04-12T15:03:39Z
dc.date.available2007-05-21
dc.date.issued2006-11-08
dc.date.submitted2007-04-25
dc.identifier.citationPavón Palacio, J. J. "Fractura y fatiga por contacto de recubrimientos de vidrio sobre Ti6Al4V para aplicaciones biomédicas". Tesi doctoral, UPC, Departament de Ciència dels Materials i Enginyeria Metal·lúrgica, 2006.
dc.identifier.isbn9788469064894
dc.identifier.otherhttp://www.tdx.cat/TDX-0425107-110816
dc.identifier.urihttp://hdl.handle.net/2117/93365
dc.description.abstractLa aleación Ti6Al4V es el biomaterial más utilizado para el reemplazo de tejidos duros, debido a su alta biocompatibilidad y a sus propiedades mecánicas. Sin embargo, al ser bioinerte no se une directamente con el hueso. Un recubrimiento de vidrio bioactivo permite un enlace directo con el hueso al precipitar hidroxiapatita (HCA) y en esta tes is doctoral se estudia el comportamiento mecánico bajo fuerzas Hertzianas de estos recubrimientos. Inicialmente se estudia un recubrimiento monocapa no bioactivo y posteriormente un recubrimiento bicapa con capa externa bioactiva y capa interna formada por el monocapa no bioactivo. La capa interna tiene un alto contenido de SiO2 para garantizar la integridad mecánica, mientras la capa externa tiene un bajo contenido de SiO2 y partículas de hidroxiapatita sintética. Cuando se aplican fuerzas de contacto monotónicas aparecen tres daños frágiles (fisuras anillo, cono y radial)seguidos por la delaminación del recubrimiento. Estos daños están influenciados por la deformación plástica del substrato, lo cual fue corroborado por comparación con vidrios monolíticos de características iguales al recubrimiento. Para el contacto estático y cíclico sobre el recubrimiento monocapa se utilizó la fisura anillo como criterio de daño. El recubrimiento se degrada bajo contacto estático debido a la corrosión bajo tensión, mientras la degradación bajo carga cíclica, observada por primera vez en éste material, se atribuye a un mecanismo de reducción del apantallamiento que ejercen in icialmente las microfisuras alrededor de la punta de las fisuras pre-existentes. <br> El carácter sinterizado del recubrimiento permite la existencia de las microfisuras en los bordes de las partículas. La formación de la fisura anillo bajo cargas tanto estáticas como cíclicas fue racionalizada a partir de las leyes de crecimiento de fisura. El primer daño en la capa externa del recubrimiento bicapa por contacto monotónico es también la fisura anillo. Ésta capa tiene menor resistencia a la fisuración anillo debido a su menor tenacidad de fractura y las mayores tensiones residuales térmicas, y se degrada bajo contacto estático y cíclico según los mismos mecanismos observados en el recubrimiento monocapa. Sin embargo, la capa externa sufre una mayor degradación bajo ambos tipos de carga, tal que, bajo carga estática, se degrada máspor su diferente composición química y por sus mayores tensiones residuales térmicas, mientras que bajo carga cíclica, la mayor degradación se debe a las diferencias microestructurales y a la mayor microfisuración asociada a las tensiones residuales térmicas. La comparación entre la respuesta al contacto monotónico, estático y cíclico en aire , del recubrimiento monocapa y de la capa externa del bicapa, demuestran la mayor resistencia de la capa interna y, por lo tanto, verifican la validez del concepto de material gradiente a partir del cual se diseñó el recubrimiento bicapa. Los ensayos de contacto sobre el recubrimiento bicapa en fluido fisiológico simulado se realizaron después de 2 meses de incubación. El contacto monotónico produjo una huella debida, tanto a la baja tenacidad como a la baja densidad de la HCA. La proyección del área dañada usada como criterio de daño para los ensayos estáticos y cíclicos, mostró la degradación del recubrimiento bajo ambos tipos de carga. La degradación por contacto cíclico fue superior debido a la participación de otros mecanismos que se suman a la corrosión bajo tensión que actúa durante el contacto estático. La evolución del daño bajo contacto estático y cíclico muestra la mayor tolerancia a medida que el daño avanza hacia el substrato. Esta característica es coherente con el comportamiento observado por comparación de la respuesta al contacto monotónico, estático y cíclico en aire entre el recubrimiento monocapa y la capa externa.
dc.description.abstractTi6Al4V alloy is the biomaterial most widely used for hard tissue replacement due to its high biocompatibility and its mechanical properties. However, it is bioinert and, therefore, does not bond directly with the bone. A bioactive glass coating allows a direct bond with the bone because of the precipitation of hydroxycarbonate apatite (HCA), and the mechanical behaviour under Hertzian forces of these coatings is studied in this doctoral thesis. The research is first addressed to a non-bioactive monolayer glass coating and later to a bilayer glass coating in which the inner layer is the same as the previous one and the outer layer is bioactive. The inner layer has a higher SiO2 content in order to ensure the mechanical stability, and the outer layer has a lower SiO2 content together with synthetic hydroxyapatite to ensure the bioactivity. The response to monotonic contact loading of the monolayer coating presents three brittle damages (ring, cone and radial cracks) and delamination of the coating. These damages are influenced by the plastic deformation of the substrate which was verified by comparison with the damage in monolithic glasses with the same composition. The ring crack was used as damage criteria for the static and cyclic contact tests. The coating is degradated under static contact due to stress corrosion, while the degradation under cyclic contact, observed by the first time in this kind of materials, is attributed to a mechanism of reduction of the shielding initially present due to a microcracked zone around the crack tip of the pre-existent cracks. The existence of microcracks at the border of the glass particles is possible due to the sintered character of the coating. The ring cracking under both static and cyclic contact was rationalized with the aid of sub-critical crack growth laws. Ring cracking is also the first damage in the outer layer of the bilayer coating during monotonic contact.<br><br/>This outer layer is less resistant to ring cracking due to both its lower fracture toughness and the higher thermal residual stress and it is degraded under static and cyclic contact loading according to the same mechanisms observed for the monolayer coating. The outer layer suffers a stronger degradation under both kinds of loading. The lower resistance under static contact is due to both its different chemical composition and its higher thermal residual stress, while the stronger degradation under cyclic contact is the consequence of both a different microstructure and more severe microcracking due to a higher thermal residual stress. The comparison of the response to monotonic, static and cyclic contact loading in air between the monolayer coating and the outer layer of the bilayer showed a higher resistance of the inner layer, which confirms the validity of the graded material concept form which the bilayer coating was designed. The contact tests of the bilayer coating in simulated body fluid were performed after 2 months of incubation to allow precipitation of HCA. The monotonic contact loading produces a residual impression in the coating due to both the low fracture toughness and the low density of the HCA layer. The projection of the damaged area used as damage criteria to study the response under static and cyclic contact loading, showed degradation under both kinds of loads. Degradation under cyclic contact loading was stronger due to existence of other mechanisms rather than the stress corrosion effect which occurs during static contact. The evolution of damages under static and cyclic contact loading showed the increase of the damage tolerance as the contact approaches to the substrate.<br> <br/>This behaviour is consistent with the results of the comparison between the response of the monolayer coating and the outer layer of the bilayer to monotnic, static and cyclic contact loading in air.
dc.language.isospa
dc.publisherUniversitat Politècnica de Catalunya
dc.rightsADVERTIMENT. L'accés als continguts d'aquesta tesi doctoral i la seva utilització ha de respectar els drets de la persona autora. Pot ser utilitzada per a consulta o estudi personal, així com en activitats o materials d'investigació i docència en els termes establerts a l'art. 32 del Text Refós de la Llei de Propietat Intel·lectual (RDL 1/1996). Per altres utilitzacions es requereix l'autorització prèvia i expressa de la persona autora. En qualsevol cas, en la utilització dels seus continguts caldrà indicar de forma clara el nom i cognoms de la persona autora i el títol de la tesi doctoral. No s'autoritza la seva reproducció o altres formes d'explotació efectuades amb finalitats de lucre ni la seva comunicació pública des d'un lloc aliè al servei TDX. Tampoc s'autoritza la presentació del seu contingut en una finestra o marc aliè a TDX (framing). Aquesta reserva de drets afecta tant als continguts de la tesi com als seus resums i índexs.
dc.sourceTDX (Tesis Doctorals en Xarxa)
dc.subjectÀrees temàtiques de la UPC::Enginyeria dels materials::Assaig de materials
dc.subject.otherimplantes
dc.subject.otherfatiga
dc.subject.otherfractura
dc.subject.otherrecubrimientos bioactivos
dc.subject.othercontacto
dc.subject.otherbiomateriales
dc.subject.otherprotesis
dc.subject.othercontacto hertziano
dc.titleFractura y fatiga por contacto de recubrimientos de vidrio sobre Ti6Al4V para aplicaciones biomédicas
dc.typeDoctoral thesis
dc.identifier.dlB.33058-2007
dc.rights.accessOpen Access
dc.description.versionPostprint (published version)
dc.identifier.tdxhttp://hdl.handle.net/10803/6051


Files in this item

Thumbnail
Thumbnail
Thumbnail
Thumbnail
Thumbnail
Thumbnail
Thumbnail
Thumbnail
Thumbnail
Thumbnail
Thumbnail
Thumbnail
Thumbnail
Thumbnail
Thumbnail
Thumbnail
Thumbnail
Thumbnail
Thumbnail

This item appears in the following Collection(s)

Show simple item record

All rights reserved. This work is protected by the corresponding intellectual and industrial property rights. Without prejudice to any existing legal exemptions, reproduction, distribution, public communication or transformation of this work are prohibited without permission of the copyright holder