Hot working analysis of a CuZn40Pb2 brass on the monophasic (beta) and intercritical (alpha plus beta) regions

Suarez, L.; Rodríguez Calvillo, Pablo; Cabrera Marrero, José M.; Martinez Romay, A; Majuelos Mallorquin, D

doi:10.1016/j.msea.2014.12.093

View/Open

manuscrito final aceptado (4,064Mb)

View Usage Statistics

Show full item record

Suarez, L.

Rodríguez Calvillo, Pablo

Cabrera Marrero, José M.

Martinez Romay, A

Majuelos Mallorquin, D

Document typeArticle

Defense date2015-03-11

Rights accessOpen Access

Abstract

The high temperature deformation behavior of a Cu4OZn2Pb brass was studied by means of compression and tensile tests in the beta monophasic and alpha/beta biphasic regions. The ductility evaluated in terms of elongation and area reduction allowed to distinguish three regions: one 13 monophasic region (above 720 degrees C), and two alpha/beta biphasic regions, between 720 degrees C and 600 degrees C, and below 600 degrees C. The fracture appearance was evolving from a ductile type, with dimple formation, to a more brittle one with grain decohesion as the deformation temperature was decreased or the amount of 13 phase reduced.; The

CitationSuarez, L., Rodriguez-Calvillo, P., Cabrera, J., Martinez, A., Majuelos, D. Hot working analysis of a CuZn40Pb2 brass on the monophasic (beta) and intercritical (alpha plus beta) regions. "Materials science and engineering A. Structural materials properties microstructure and processing", 11 Març 2015, p. 42-50.

URIhttp://hdl.handle.net/2117/76728

DOI10.1016/j.msea.2014.12.093

ISSN0921-5093

Collections

View Usage Statistics

Show full item record

Files	Description	Size	Format	View
Markedup_Manuscript.docx	manuscrito final aceptado	4,064Mb	Microsoft Word 2007	View/Open

Except where otherwise noted, content on this work is licensed under a Creative Commons license: Attribution-NonCommercial-NoDerivs 3.0 Spain

UPCommons. Global access to UPC knowledge