Wear resistance and friction analysis of Ti6Al4V cylindrical ball-burnished specimens with and without vibration assistance
Visualitza/Obre
Cita com:
hdl:2117/385375
Tipus de documentArticle
Data publicació2023-02-01
EditorSpringer Nature
Condicions d'accésAccés obert
Llevat que s'hi indiqui el contrari, els
continguts d'aquesta obra estan subjectes a la llicència de Creative Commons
:
Reconeixement 4.0 Internacional
Abstract
The objective of the research is to analyze the impact of the ultrasonic vibration assistance on the wear resistance due to the topography enhancement caused on Ti6Al4V cylindrical samples after surface modification through a ball burnishing process. The process parameters considered for this study are the burnishing force, the number of passes, and the addition of a 40 kHz ultrasonic assistance, which are thought to enhance the surface topography and increase the hardener effect in terms of depth. A complete screening design of 3 factors was performed, revealing that the number of passes and the vibration assistance are the most important parameters for minimizing the wear volume loss, being 170 N of burnishing force, 3 passes, and the addition of the vibration assistance as the best combination found. However, no significant difference in the friction force was observed. The topography results show that there is a decrease in the average roughness from 1.50 to 0.45 µm with optimal burnishing conditions. It was also analyzed the microstructure originated after the turning, the conventional ball burnishing, and the vibration-assisted ball burnishing, being the last optimal in terms of depth affectation to the microstructure. Therefore, these results confirm an improvement in terms of wear enhancement, friction reduction, and topography results when vibration assistance is added to a conventional ball burnishing process.
CitacióVelazquez, E. [et al.]. Wear resistance and friction analysis of Ti6Al4V cylindrical ball-burnished specimens with and without vibration assistance. "The international journal of advanced manufacturing technology", 1 Febrer 2023, vol. 2023, p. 1-12.
ISSN1433-3015
Versió de l'editorhttps://link.springer.com/article/10.1007/s00170-023-10919-y
Col·leccions
- Departament d'Enginyeria mecànica - Articles de revista [596]
- Doctorat en Enginyeria Mecànica, Fluids i Aeronàutica - Articles de revista [149]
- Departament de Ciència i Enginyeria de Materials - Articles de revista [734]
- TECNOFAB - Grup de Recerca en Tecnologies de Fabricació - Articles de revista [206]
Fitxers | Descripció | Mida | Format | Visualitza |
---|---|---|---|---|
s00170-023-10919-y.pdf | 2,324Mb | Visualitza/Obre |