Delayed elasticity of metallic glasses: Loading time and temperature dependences of the anelastic relaxation
Visualitza/Obre
10.1103/PhysRevMaterials.6.125601
Inclou dades d'ús des de 2022
Cita com:
hdl:2117/379223
Tipus de documentArticle
Data publicació2022-12-09
EditorAmerican Physical Society (APS)
Condicions d'accésAccés obert
Llevat que s'hi indiqui el contrari, els
continguts d'aquesta obra estan subjectes a la llicència de Creative Commons
:
Reconeixement-NoComercial-SenseObraDerivada 4.0 Internacional
Abstract
One of the hallmarks of disordered matter is the large amplitude of the anelastic deformation, i.e., the fraction of reversible deformation that is not instantaneously recovered after the release of load but is delayed in time. In this paper, this delayed elasticity is studied for the glass-forming Zr46.25Ti8.25Cu7.5Ni10Be27.5 alloy by means of stress step and recovery experiments. Even at high temperatures, not far from the glass transition, the delayed elasticity can recover an important fraction of the deformation and endure for a long time. Analyzing the effects of loading time and waiting time on the strain evolution, we reveal the presence of an anelastic response with a timescale dependent on loading time and an invariant shape, which indicates the presence of a distribution of reversible relaxation modes following a t-n law with exponent n between 0.5 and 1. The underlying distribution of energy barriers activated at different temperatures is accordingly shape invariant. Moreover, we found that a distribution of reversible modes corresponding to the high-frequency side of the a-relaxation peak can reproduce the experimental results. The results establish a direct link between the dynamical spectrum and the distribution of activation energies, revealing the origin of the transient creep and anelastic recovery behaviors of metallic glasses.
CitacióNabahat, M. [et al.]. Delayed elasticity of metallic glasses: Loading time and temperature dependences of the anelastic relaxation. "Physical review materials", 9 Desembre 2022, vol. 6, núm. 12, article 125601, p. 1-11.
ISSN2475-9953
Col·leccions
Fitxers | Descripció | Mida | Format | Visualitza |
---|---|---|---|---|
PhysRevMaterials.6.125601.pdf | 2,703Mb | Visualitza/Obre |