Plane-strain fracture toughness of thin additively manufactured maraging steel samples
Visualitza/Obre
Santos et al. - 2022 - Plane-strain fracture toughness of thin additively manufactured maraging steel samples.pdf (12,63Mb) (Accés restringit)
Sol·licita una còpia a l'autor
Què és aquest botó?
Aquest botó permet demanar una còpia d'un document restringit a l'autor. Es mostra quan:
- Disposem del correu electrònic de l'autor
- El document té una mida inferior a 20 Mb
- Es tracta d'un document d'accés restringit per decisió de l'autor o d'un document d'accés restringit per política de l'editorial
10.1016/j.addma.2021.102509
Inclou dades d'ús des de 2022
Cita com:
hdl:2117/368057
Tipus de documentArticle
Data publicació2021-11-24
EditorElsevier
Condicions d'accésAccés restringit per política de l'editorial
Tots els drets reservats. Aquesta obra està protegida pels drets de propietat intel·lectual i
industrial corresponents. Sense perjudici de les exempcions legals existents, queda prohibida la seva
reproducció, distribució, comunicació pública o transformació sense l'autorització del titular dels drets
Abstract
This study aimed to evaluate the aging effects on mechanical properties of 18Ni (300) maraging steel processed by additive manufacturing powder bed fusion and subjected to different aging conditions. The aging temperatures were 470 °C, 510 °C, and 530 °C, with exposure times ranging from 0.33 to 96 h, followed by air cooling. Despite the layer-by-layer material consolidation mechanism, weak preferred orientation was found in the as-built condition; moreover, only martensite and austenite were found in the X-ray diffraction results. This alloy showed a steep increase in hardness, compressive strength, and tensile strength, while the work-hardening ability decreased with aging. Despite using thin single-edge bending samples (5 mm), the plane-strain fracture toughness (KIC) size requirement was met, and valid KIC results were 49 ~ 64 . This result could help design new additive manufacturing applications of high-strength steel, such as thin-walled, lattice structures, and reduced cross-section parts projected to minimize weight in different industries.
CitacióSantos, P. [et al.]. Plane-strain fracture toughness of thin additively manufactured maraging steel samples. "Additive manufacturing", 24 Novembre 2021, vol. 49, núm. Article 102509.
ISSN2214-8604
Fitxers | Descripció | Mida | Format | Visualitza |
---|---|---|---|---|
Santos et al. - ... maraging steel samples.pdf | 12,63Mb | Accés restringit |