Analysis and evaluation of corrosion in naval steels
Visualitza/Obre
Estadístiques de LA Referencia / Recolecta
Inclou dades d'ús des de 2022
Cita com:
hdl:2117/356424
Tipus de documentArticle
Data publicació2021
EditorSARTI
Condicions d'accésAccés obert
Llevat que s'hi indiqui el contrari, els
continguts d'aquesta obra estan subjectes a la llicència de Creative Commons
:
Reconeixement-NoComercial-SenseObraDerivada 3.0 Espanya
Abstract
The corrosion of steel due to seawater is a problem faced by all ships. In this work it has been analyzed two of the variables that most infuence the degradation process of carbon steels in marine environments (pH and chloride concentration), as well as the galvanic couple, which arises when two metals of diferent potential make contact. The study was carried out with two types of steel (S275JR and S235JR) and 15 diferent environments were analyzed (Fig. 1). The progression of corrosion was evaluated in two ways: i) by measuring the mass variation due to the corrosion phenomenon, which was subsequently used to determine the kinetics of the reaction, and ii) visually, by using free software ImageJ. The combined efect of the three variables was analyzed using the Statistics software, performing a factorial analysis in order to obtain response surfaces and their corresponding predictive equations, which allow predicting the efect of corrosion. Finally, in order to observe the diferences between the model obtained and the degree of actual corrosion, both steel types were subjected to the efect of seawater from the dock of the Naval Academy. Results of the study showed a loss of 0,1 g a week, infuenced by the chloride concentration and the acid environment (Fig. 2). From the data obtained, predictive equations were formulated and compared with experiments in laboratory. After 3 weeks of corrosion induced in laboratory, a deviation of 6,74% between the real and predicted mass of probes was observed for steel S275JR and 1,35% for steel S235JR, which evidence the accuracy of the experiments carried out and gives a valuable tool in order to predict efects of corrosion. Corrosion kinetics showed a degradation of 0,3 mm/year and predictive equations showed a deviation lower than 7% in both steels when compared with experiments in laboratory.
CitacióDevesa Rey, R.; Montesinos, M.E. Analysis and evaluation of corrosion in naval steels. 9th International Workshop on Marine Technology (MARTECH 2021)". ""Instrumentation Viewpoint", 2021, núm. 21, p. 78.