Study of the fire and thermal behaviour of façade panels made of natural fibre-reinforced cement-based composites
10.1016/j.conbuildmat.2021.124195
Inclou dades d'ús des de 2022
Cita com:
hdl:2117/349662
Tipus de documentArticle
Data publicació2021-07-13
EditorElsevier
Condicions d'accésAccés obert
Llevat que s'hi indiqui el contrari, els
continguts d'aquesta obra estan subjectes a la llicència de Creative Commons
:
Reconeixement 3.0 Espanya
Abstract
The thermal and fire behaviour of calcium aluminate cement-based composites with a variable metakaolin content (from 0 to 40 wt% addition) reinforced with nonwoven flax fabrics has been examined. The fire behaviour was assessed using epiradiator and small-scale fire testing. The composites did not emit smoke or generate flames, nor did they produce spalling. Their integrity was maintained above 1000 ¿C. Samples having a higher metakaolin content revealed a delay in the temperature of the unexposed surface until reaching 760 ¿C. The effect of exposure to high temperatures (250 ¿C, 450 ¿C, and 950 ¿C) on bending behaviour was examined. The fibres were found to maintain their reinforcing capacity up to 250 ¿C, while the matrix maintained its performance up to 450 ¿C. The addition of metakaolin reduced conductivity and diffusivity. The results of the thermal and fire behaviour of the tested composites indicated that they may be suitable for façade panels for outdoor applications
CitacióGonzalez, L. [et al.]. Study of the fire and thermal behaviour of façade panels made of natural fibre-reinforced cement-based composites. "Construction and building materials", 13 Juliol 2021, vol. 302, p. 124195:1-124195:13.
ISSN0950-0618
Versió de l'editorhttps://www.sciencedirect.com/science/article/pii/S0950061821019553
Col·leccions
- GICITED - Grup Interdiciplinari de Ciència i Tecnologia en l'Edificació - Articles de revista [190]
- TECTEX - Grup de recerca en Tecnologia Tèxtil - Articles de revista [160]
- Departament de Tecnologia de l'Arquitectura - Articles de revista [556]
- Departament de Ciència i Enginyeria de Materials - Articles de revista [729]
- Doctorat en Enginyeria Tèxtil i Paperera - Articles de revista [30]
- Departament d'Enginyeria Agroalimentària i Biotecnologia - Articles de revista [1.045]
Fitxers | Descripció | Mida | Format | Visualitza |
---|---|---|---|---|
Gonzalez Lopez, ... ement based composites.pdf | 15,62Mb | Visualitza/Obre |