dc.contributor.authorFargas Ribas, Gemma
dc.contributor.authorSosa, D.
dc.contributor.authorTarragó, José María
dc.contributor.authorTarrés Puit, Elena
dc.contributor.authorFair, Jonathan
dc.contributor.authorLlanes Pitarch, Luis Miguel
dc.contributor.otherUniversitat Politècnica de Catalunya. Departament de Ciència i Enginyeria de Materials
dc.date.accessioned2020-09-25T12:56:21Z
dc.date.issued2020-05-27
dc.identifier.citationFargas, G. [et al.]. Influence of the microstructure on corrosion induced damage of WC-Co cemented carbides. "Powder metallurgy", 27 Maig 2020, vol. 63, núm. 3, p. 174-179.
dc.identifier.issn0032-5899
dc.identifier.urihttp://hdl.handle.net/2117/329263
dc.description.abstractThe main goal of the present work is to study the influence of the microstructure on the corrosion behavior of cemented carbides WC-Co in two corrosive media. Corrosion kinetics were determined by immersion tests while the electrochemical evolution of the Surface was analyzed using impedance testing. Damage tolerance to corrosion was evaluated by assessing fracture strength on specimens previously subjected to corrosion. Results pointed out that for both grades the corrosion rate was higher in seawater, being more significant for the grade with a medium grain size. The corrosion phenomenon that took place in both media was caused by the oxidation reaction of cobalt. In seawater, the polarization resistance decreased for both grades whereas in mine water increased, due to the formation of a layer of corrosion products, which slowed down the cobalt dissolution process in Surface. In both media, a greater strength loss of the ultrafine grades was evidenced.
dc.format.extent6 p.
dc.language.isoeng
dc.rightsAttribution-NonCommercial-NoDerivs 3.0 Spain
dc.rights.urihttp://creativecommons.org/licenses/by-nc-nd/3.0/es/
dc.subjectÀrees temàtiques de la UPC::Enginyeria dels materials::Metal·lúrgia
dc.subject.lcshCarbides
dc.subject.lcshCorrosion and anti-corrosives
dc.subject.otherCemented carbides
dc.subject.otherCorrosion kinetics
dc.subject.otherSea water
dc.subject.otherMine water
dc.titleInfluence of the microstructure on corrosion induced damage of WC-Co cemented carbides
dc.typeArticle
dc.subject.lemacCarburs
dc.subject.lemacCorrosió i anticorrosius
dc.contributor.groupUniversitat Politècnica de Catalunya. CIEFMA - Centre d'Integritat Estructural, Micromecànica i Fiabilitat dels Materials
dc.identifier.doi10.1080/00325899.2020.1768354
dc.description.peerreviewedPeer Reviewed
dc.relation.publisherversionhttps://www.tandfonline.com/doi/abs/10.1080/00325899.2020.1768354
dc.rights.accessRestricted access - publisher's policy
local.identifier.drac29187733
dc.description.versionPostprint (author's final draft)
dc.date.lift2021-05-20
local.citation.authorFargas, G.; Sosa, D.; Tarragó, J.M.; Tarrés, E.; Fair, J.; Llanes, L.
local.citation.publicationNamePowder metallurgy
local.citation.volume63
local.citation.number3
local.citation.startingPage174
local.citation.endingPage179


Files in this item

Thumbnail

This item appears in the following Collection(s)

Show simple item record

Attribution-NonCommercial-NoDerivs 3.0 Spain
Except where otherwise noted, content on this work is licensed under a Creative Commons license : Attribution-NonCommercial-NoDerivs 3.0 Spain