Relaxation of internal friction and shear viscosity in Zr57Nb5Al10Cu15.4Ni12.6 metallic glass
Rights accessOpen Access
Except where otherwise noted, content on this work is licensed under a Creative Commons license : Attribution-NonCommercial-NoDerivs 3.0 Spain
Relaxation of internal friction of Zr57Nb5Al10Cu15.4Ni12.6 metallic glass was investigated by mechanical spectroscopy. The stress relaxation of internal friction with different aging temperature was described by Kohlrausch-Williams-Watts (KWW) equation. The shear viscosity behavior during linear heating can be interpreted as a result of the local irreversible structural relaxation with distributed activation energies. The results show that the dynamic heterogeneity and the atomic mobility are stimulated by the increasing annealing temperature.
CitationDuan, Y.J. [et al.]. Relaxation of internal friction and shear viscosity in Zr57Nb5Al10Cu15.4Ni12.6 metallic glass. "Intermetallics", 1 Setembre 2020, vol. 124, p. 106846:1-106846:6.