Nonlinear dielectric response of BaBi4Ti4O15 ceramics
Tipo de documentoComunicación de congreso
Fecha de publicación2012
EditorAmerican Institute of Physics (AIP)
Condiciones de accesoAcceso restringido por política de la editorial
Nonlinear dielectric response of BaBi4Ti4O15 ceramics synthesized via the conventional solid-state reaction route has been monitored over a wide range of electric field strengths (E0 = 0.5-5 kV/cm). Dielectric permittivity was found to increase linearly within the range of applied field. Rayleigh relations were employed to interpret the nonlinear dielectric response and the contribution of irreversible domain wall motion to the macroscopic permittivity was separated. The values of room temperature Rayleigh dielectric coefficient (α) and relative initial permittivity (ε′init) were found to be 2.28±0.02 cm/kV and 146.10±0.07, respectively. A reasonable agreement between the simulated and measured polarization-electric field (P-E) hysteresis loops was observed at an applied electric field of 5 kV/cm.
CitaciónKumar, S. [et al.]. Nonlinear dielectric response of BaBi4Ti4O15 ceramics. A: SOLID STATE PHYSICS SYMPOSIUM. "PROCEEDINGS OF THE 57TH DAE SOLID STATE PHYSICS SYMPOSIUM 2012". Bombay: American Institute of Physics (AIP), 2012, p. 998-999.
|Sunil Nonlinear Dielectric Response of BaBi4.pdf||783.2Kb||Acceso restringido|