Polyaniline coated core-shell polyacrylates: Control of film formation and coating application for corrosion protection
POC_2019_P Bertuoli et al_[Postprint].pdf (2,715Mb) (Restricted access) Request copy
Què és aquest botó?
Aquest botó permet demanar una còpia d'un document restringit a l'autor. Es mostra quan:
- Disposem del correu electrònic de l'autor
- El document té una mida inferior a 20 Mb
- Es tracta d'un document d'accés restringit per decisió de l'autor o d'un document d'accés restringit per política de l'editorial
Rights accessRestricted access - publisher's policy (embargoed until 2023-03-01)
Aqueous polymer colloidal nanoparticles, composed by poly(methyl metacrylate), butyl acrylate, and acrylic acid, as “core” (P(MMA/BA/AA)); and polyaniline (PAni) doped with dodecylbenzenesulfonic acid (DBSA), as “shell”, were prepared. The complete synthesis consisted of two-steps. In the first step P(MMA/BA/AA) particles were obtained in a semi-continuous process by free radical emulsion polymerization, followed by a second step where the chemical oxidative polymerization of aniline monomers upper the “core” surfaces occurred. Transmission electron microscopy images (TEM) and dinamic light scattering (DLS) confirmed the obtaining of spherical nanoparticles, which are stable for further free solid film preparation and coatings for metal protection. The free films were characterized by FTIR, Raman, UV–vis, X-Ray photoelectron spectroscopy (XPS), differential scanning calorimetry (DSC), thermogravimetry (TGA), optical and scanning electron microscopy (SEM), static contact angle, mechanical properties and water absorption. The metal protection was evaluated after check the adhesion properties and the impedance parameters. The presence of a low concentration of PAni-DBSA (3¿wt. %) on the acrylic polymer altered the hydrophilicity and the water uptake properties of the coatings without affecting the capability of obtaining passive layers for the protection of phosphatized carbon steel surface against corrosion, even after almost 20 days of immersion in NaCl aggressive solutions.
CitationBertuoli, P. [et al.]. Polyaniline coated core-shell polyacrylates: Control of film formation and coating application for corrosion protection. "Progress in organic coatings", 1 Març 2019, vol. 128, p. 40-51.