dc.description.abstract[CATALÀ] L’objectiu principal d’aquest treball és fer-ne un estudi dels diferents elements d’aliatge afegits al AlSi9Cu3, també designat com EN AC 46500. Aquets elements són el Zn, Mg, Cr, Zr i el refinant de gra TiB que s’afegeixen en petites quantitats. La intenció es millorar les propietats mecàniques del material base. Es realitzen distintes colades d’aquests microaliatges, dels quals es vol saber quin és el pic de duresa més alt en un temps de maduració més curt després de realitzar-li un tractament T6. Aquest tractament tèrmic té una posta en solució de 515°C durant 6h seguit d’un tremp amb aigua i posteriorment una maduració artificial a 170°C durant vuit intervals de temps diferents. Aquests paràmetres venen definits per resultats obtinguts en estudis previs. Per comprovar l’efectivitat del T6 s’han analitzat les dureses i s’han realitzat micrografies. Amb les mostres de les dureses s’ha pogut determinar que l’aliatge AlSi9Cu3 + 3 %Zn + 2%Mg + 0,2% Cr + 0,2% Zr presenta un major pic de duresa en menys temps que la resta de les colades. Amb aquest aliatge s’ha realitzat una colada major per fer un assaig de tracció i comparar la resistència a tracció de l’aliatge modificat amb l’aliatge base. L’assaig no ha sigut satisfactori degut a les impureses (òxids i porositats) de les provetes sorgides durant la fabricació. No obstant, s’ha pogut comprovar un lleuger augment de la resistència a la tracció en l’aliatge modificat.
dc.description.abstract[ANGLÈS] The main objective of this work is to realize a study of the different alloy elements added to AlSi9Cu3, also designated as EN AC 46500. These elements are Zn, Mg, Cr, Zr and the grain refiner TiB which are added in small amounts. The intention is to improve the mechanical properties of the base material. Different casts are made of these micro-alloys, which are intended to know what is the highest peak strength in a shorter aging time after performing a T6 treatment. This heat treatment has a temperature solution of 515 ° C for 6 hours followed by a quench with water and then an artificial aging at 170 ° C for eight different time intervals. These parameters are defined by results obtained in previous studies. To verify the effectiveness of the T6, the hardness has been analyzed and micrographs have been performed. With the samples of the hardness it has been possible to determine that the alloy AlSi9Cu3 + 3% Zn + 2% Mg + 0.2% Cr + 0.2% Zr presents a greater peak of hardness in less time than the rest of the casts With this alloy, a larger leakage has been performed to perform a tensile test and compare the tensile strength of the modified alloy with the base alloy. The test has not been satisfactory due to the impurities (oxides and porosities) of the test tubes produced during manufacture. However, it has been possible to check a slight increase in the tensile strength in the modified alloy.
dc.language.isocat
dc.publisherUniversitat Politècnica de Catalunya
dc.rightsAttribution-NonCommercial-NoDerivs 3.0 Spain
dc.rights.urihttp://creativecommons.org/licenses/by-nc-nd/3.0/es/
dc.subjectÀrees temàtiques de la UPC::Enginyeria dels materials
dc.subject.lcshAlloys -- Microstructure
dc.subject.lcshAlloys -- Thermal properties
dc.subject.otherAliatges d’alumini
dc.subject.otherTractaments tèrmics
dc.subject.otherMicroaliatge
dc.subject.otherPropietats mecàniques
dc.subject.otherCoure
dc.subject.otherSilici
dc.subject.otherAluminum Alloys
dc.subject.otherCopper
dc.subject.otherSilicon
dc.subject.otherHeat treatments
dc.subject.otherMicroalloy
dc.subject.otherMechanical properties
dc.titleOptimització aliatges Al-Si-Cu microaliats
dc.typeBachelor thesis
dc.subject.lemacAliatges -- Microestructura
dc.subject.lemacAliatges -- Propietats tèrmiques
dc.rights.accessOpen Access
dc.audience.educationlevelGrau
dc.audience.mediatorEscola Politècnica Superior d'Enginyeria de Vilanova i la Geltrú


Files in this item

Thumbnail
Thumbnail
Thumbnail

This item appears in the following Collection(s)

Show simple item record

Except where otherwise noted, content on this work is licensed under a Creative Commons license: Attribution-NonCommercial-NoDerivs 3.0 Spain