dc.contributor.authorMestra Rodríguez, Álvaro Miguel
dc.contributor.authorHvizdos, Pavol
dc.contributor.authorValle Chiro, Jorge Antonio
dc.contributor.authorAnglada Gomila, Marcos Juan
dc.contributor.otherUniversitat Politècnica de Catalunya. Departament de Ciència dels Materials i Enginyeria Metal·lúrgica
dc.date.accessioned2010-11-15T13:44:46Z
dc.date.available2010-11-15T13:44:46Z
dc.date.created2009
dc.date.issued2009
dc.identifier.citationMestra, A. [et al.]. Mecanismos de desgaste en policristales de circona dopada con 3% molar de itria. "Anales de mecánica de la fractura", 2009, vol. 29, p. 81-86.
dc.identifier.issn0213-3725
dc.identifier.urihttp://hdl.handle.net/2117/10293
dc.description.abstractEn el presente trabajo se estudia el comportamiento tribológico de policristales de circona dopada con 3% molar de itria con diferente tamaño de grano utilizando la técnica de desgaste por deslizamiento de bola sobre disco a diferentes velocidades. Se identifican los regímenes de desgaste en función de la velocidad y se ha encontrado que el daño ocurrido aumenta significativamente al aumentar la velocidad de deslizamiento. La transición del desgaste suave a severo ocurre a 10-5 mm3/mN, la cual coincide con los datos de la literatura. Los mecanismos de desgaste se discuten en detalle en función del régimen de desgaste. Se ha constatado que en el régimen de desgaste suave ambos materiales se comportan de forma similar mientras que, en el régimen de desgaste severo el material con tamaño de grano más pequeño presenta mejor resistencia al desgaste.-------- This paper studies the tribological behaviour of zirconia polycrystals stabilised by 3% of yttria with different grain size using a ball on disc technique in dry conditions at different sliding speeds. The wear regimes as a function of speed have been identified. The wear damage increased significantly with increasing sliding speed. The mild to severe wear transition occurred at the wear rate of 10-5 mm3/mN which is in accordance with literature data. The wear damage micromechanisms corresponding to various degrees of wear have been studied and discussed in detail. It has been found that at the low wear regime both materials behave identically while under more severe conditions the material with finer grains exhibited better wear resistance.
dc.format.extent6 p.
dc.language.isospa
dc.subjectÀrees temàtiques de la UPC::Enginyeria dels materials::Desgast de materials
dc.subject.lcshZirconium oxide -- Experiments
dc.titleMecanismos de desgaste en policristales de circona dopada con 3% molar de itria
dc.typeArticle
dc.subject.lemacZirconia
dc.contributor.groupUniversitat Politècnica de Catalunya. CIEFMA - Centre d'Integritat Estructural, Micromecànica i Fiabilitat dels Materials
dc.description.peerreviewedPeer Reviewed
dc.rights.accessRestricted access - publisher's policy
local.identifier.drac4271765
dc.description.versionPostprint (published version)
local.citation.authorMestra, A.; Hvizdos, P.; Valle, J.; Anglada, M.
local.citation.publicationNameAnales de mecánica de la fractura
local.citation.volume29
local.citation.startingPage81
local.citation.endingPage86


Files in this item

Thumbnail

This item appears in the following Collection(s)

Show simple item record

All rights reserved. This work is protected by the corresponding intellectual and industrial property rights. Without prejudice to any existing legal exemptions, reproduction, distribution, public communication or transformation of this work are prohibited without permission of the copyright holder