dc.description.abstractcrisis present in the world. solution processing of such devices allows large scale production using roll-to-roll process and similar fabrication processes. Lasers can be used for selective ablation of different layer of such solar cells for structuring. This work aimed at fabricating flexible polymer solar cells with all layer processed from solution as well as investigating the effect of laser for structuring different layer of the solar cells fabricated. To fabricate the solar cells, well-established photoactive blends from poly-(3-hexylthiophene-2,5-diyl) and [6,6]-phenyl C61-butyric acid methyl ester (P3HT:PC61BM) was used. The solar cells were comprised of solution processed silver as cathode and poly(3,4-ethylenedioxythiophene):poly(styrenesulfonate) (PEDOT: PSS) as anode while zinc oxide (ZnO) was used as electron transport layer. An infrared laser was used to structure different layers of the solar cells and assess the effect on the layers. For fabrication, different layers were processed by lab-scale solution-based techniques such as doctor-blading, horizontal dipping and spin coating. Processing parameters for fabricating each layer were optimized experimentally and the solar cell fabricated with optimal parameters showed reasonable power conversion efficiency. Also, the analysis of structuring different layer of solar cells using an infrared laser is presented.
dc.publisherUniversitat Politècnica de Catalunya
dc.titleSolution Processed Organic Solar Cells: Fabrication and Laser Structuring
dc.typeMaster thesis
dc.rights.accessRestricted access - author's decision
dc.audience.mediatorEscola Tècnica Superior d'Enginyeria Industrial de Barcelona

Ficheros en el ítem

Imagen en miniatura

Este ítem aparece en la(s) siguiente(s) colección(ones)

Mostrar el registro sencillo del ítem

Todos los derechos reservados.Esta obra está protegida por los derechos de propiedad intelectual e industrial. Sin perjuicio de las exenciones legales existentes, queda prohibida su reproducción, distribución, comunicación pública o transformación sin la autorización del titular de los derechos