Study of stress corrosion cracking resistance of ultrafinegrained zirconium alloys
dc.contributor | Nikulin, S.A. |
dc.contributor.author | Nogués Martín, Pere |
dc.date.accessioned | 2012-10-23T19:28:19Z |
dc.date.issued | 2011 |
dc.identifier.uri | http://hdl.handle.net/2099.1/16357 |
dc.description.abstract | A method (approach) have been developed for SCC tests of sheet specimens from zirconium alloys which includes: exposure in iodine-methanol solution, quantitative analysis of corrosion defects, tensile tests of corroded specimens and quantitative analysis of fracture surfaces and cross sections. A comparison was made between sheets of as-received and ultrafinegrained zirconium alloys for nuclear reactors to discuss its applicability in the nuclear industry. |
dc.language.iso | eng |
dc.publisher | Universitat Politècnica de Catalunya |
dc.publisher | National University of Science and Technology MISIS |
dc.subject | Àrees temàtiques de la UPC::Enginyeria dels materials::Assaig de materials::Assaig de fractura |
dc.subject | Àrees temàtiques de la UPC::Enginyeria dels materials::Assaig de materials::Assaigs de corrosió |
dc.subject | Àrees temàtiques de la UPC::Enginyeria dels materials::Metal·lúrgia |
dc.subject.lcsh | Zirconium alloys -- Microstructure |
dc.subject.lcsh | Zirconium alloys – Corrosion |
dc.subject.lcsh | Zirconium alloys – Cracking and Fracture |
dc.title | Study of stress corrosion cracking resistance of ultrafinegrained zirconium alloys |
dc.type | Master thesis (pre-Bologna period) |
dc.subject.lemac | Zirconi – Aliatges -- Microestructura |
dc.subject.lemac | Zirconi – Aliatges -- Corrosió |
dc.subject.lemac | Zirconi – Aliatges -- Fissuració i Fractura |
dc.rights.access | Restricted access - author's decision |
dc.date.lift | 10000-01-01 |
dc.audience.educationlevel | Estudis de primer/segon cicle |
dc.audience.mediator | Escola Tècnica Superior d'Enginyeria Industrial de Barcelona |
dc.audience.degree | ENGINYERIA DE MATERIALS (TITULACIÓ CONJUNTA AMB LA UB) (Pla 2003) |
dc.description.mobility | Outgoing |