PLA/SiO2 composites: influence of the filler modifications on the morphology, crystallization behaviour and mechanical properties
Bin Raja-Nazri, Raja Nazrul Hakim; Cailloux, Jonathan; Santana Pérez, Orlando Onofre; Bou Serra, Jordi; Sánchez Soto, Miguel; Odent, Jeremy; Raquez, Jean-Marie; Dubois, Philippe; Carrasco Alonso, Félix Ángel; Maspoch Rulduà, Mª Lluïsa (Wiley, 2017-06-14)
Article
Open AccessFilms of an architecturally modified poly(lactic acid) (PLAREx) with three different types of fumed silica nanofillers (SiO2) were processed through reactive extrusion-calendering in a pilot plant. The effects of the SiO2 ... -
Preparation and characterization of nanocomposites based on polylactide manufactured by reactive extrusion-calendering : thermal, rheological, mechanical and fracture properties
Bin Raja-Nazri, Raja Nazrul Hakim (Universitat Politècnica de Catalunya, 2018-06-01)
Doctoral thesis
Open AccessPLA nanocomposites sheets that is rnodified with multi-functional epoxide reactive agent (Joncryi4300F, BASF, Germany) were manufacturad using reactive extrusion in a pilot plant. A commercial grade of PLA (PLA 40320, ... -
Production of poly(carbonate-co-ether) via catalytic polymerization of epoxidized linseed oil, propylene oxide and carbon dioxide
Bou Serra, Jordi; Binti Shaarani, Farra Wahida; Bin Raja-Nazri, Raja Nazrul Hakim (Institute of Physics (IOP), 2019-08-27)
Article
Open AccessPoly-(carbonate-co-ether) was synthesized via catalytic polymerization between epoxidized linseed oil (ELO), propylene oxide (PO) and carbon dioxide (CO2) using heterogeneous catalyst namely Co-Zn double metal cyanide ... -
Reactive extrusion: A useful process to manufacture structurally modified PLA/o-MMT composites
Cailloux, Jonathan; Bin Raja-Nazri, Raja Nazrul Hakim; Santana Pérez, Orlando Onofre; Bou, Jordi; Abt, Tobias Martin; Sánchez Soto, Miguel; Carrasco, Felix; Maspoch Rulduà, Mª Lluïsa (2016-05-26)
Article
Open AccessIn the present work, poly(lactic acid) (PLA) sheets reinforced with organically modified montmorillonite (o-MMT) were manufactured through reactive extrusion-calendering using a masterbatch approach in a pilot plant. ... -
Sheets of poly(lactide)/o-MMT prepared by one-step reactive extrusion-calendering process
Cailloux, Jonathan; Bin Raja-Nazri, Raja Nazrul Hakim; Santana Pérez, Orlando Onofre; Sánchez Soto, Miguel; Franco-Urquiza, Edgar; Carrasco Alonso, Félix Ángel; Maspoch Rulduà, Mª Lluïsa (Universidad de Sevilla. Grupo de Elasticidad y Resistencia de Materiales, 2014)
Conference report
Open AccessIn this study, a reactive extrusion-calendering process was used in order to manufacture OMMT-based (2.5 wt.%) PLA-REX sheets with a nominal thickness of 1 mm. During processing, the properties of the melt were stabilized ...