Focused Ion Beam tomography of the damage produced in zirconia toughened alumina
Visualitza/Obre
Estadístiques de LA Referencia / Recolecta
Inclou dades d'ús des de 2022
Cita com:
hdl:2099.1/24506
Tipus de documentProjecte Final de Màster Oficial
Data2014-09
Condicions d'accésAccés obert
Llevat que s'hi indiqui el contrari, els
continguts d'aquesta obra estan subjectes a la llicència de Creative Commons
:
Reconeixement-NoComercial-SenseObraDerivada 3.0 Espanya
Abstract
Two different three-dimensional reconstructions of the crack propagation
induced by mechanical testing in zirconia-toughened alumina (ZTA) were made. The first tomography is of the damage caused by an indentation, with the objective to visualize how the crack propagates inside of the material and how it interacts with the different phases that compose the material. The second reconstruction is based on the damage caused by a scratch test on the surface of the material and the fissures generated. By doing a Focused Ion Beam (FIB) tomography it is possible to understand what happens inside of the material when a mechanical test is performed, instead of just the surface. From the fissures obtained by both the indentation and the scratch
tests, it can be calculated if the crack has a phase propagation tendency, the tortuosity of the crack, the crack opening displacement and a complete characterization of the material. Also, the precise reconstruction of the microstructure and geometry of the different phase grains is possible. A
comparison between the two samples is done regarding all the previously mentioned aspects to study.
MatèriesZirconium alloys -- Microstructure, Zirconium alloys – Cracking and Fracture, Focused ion beams, Tomography -- Industrial applications, Zirconi – Aliatges -- Microestructura, Zirconi – Aliatges -- Fissuració i Fractura, Feixos d’ions focalitzats, Tomografia -- Aplicacions industrials
TitulacióMÀSTER UNIVERSITARI EN CIÈNCIA I ENGINYERIA DE MATERIALS (Pla 2014)