Substrate surface finish effects on scratch resistance and failure mechanisms of TiN-coated hardmetals
dc.contributor.author | Yang, Jing |
dc.contributor.author | Roa Rovira, Joan Josep |
dc.contributor.author | Odén, Magnus |
dc.contributor.author | Johansson Joesaar, M.P |
dc.contributor.author | Esteve, Joan |
dc.contributor.author | Llanes Pitarch, Luis Miguel |
dc.contributor.other | Universitat Politècnica de Catalunya. Departament de Ciència dels Materials i Enginyeria Metal·lúrgica |
dc.date.accessioned | 2016-05-05T10:41:34Z |
dc.date.available | 2017-03-15T01:30:46Z |
dc.date.issued | 2015-03-15 |
dc.identifier.citation | Yang, J., Roa, J.J., Oden, M., Johansson, M., Esteve, J., Llanes, L. Substrate surface finish effects on scratch resistance and failure mechanisms of TiN-coated hardmetals. "Surface and coatings technology", 15 Març 2015, vol. 265, p. 174-184. |
dc.identifier.issn | 0257-8972 |
dc.identifier.uri | http://hdl.handle.net/2117/86628 |
dc.description.abstract | In this study, the influence of substrate surface finish on scratch resistance and associated failure mechanisms is investigated in the case of a TiN-coated hardmetal. Three different surface finish conditions are studied: as-sintered (AS), ground (G), and mirror-like polished (P). For G conditioned samples, scratch tests are conducted both parallel and perpendicular to the direction of the grinding grooves. It is found that coated AS, G and P samples exhibit similar critical load for initial substrate exposure and the same brittle adhesive failure mode. However, the damage scenarios are different, i.e. the substrate exposure is discrete and localized to the scratch tracks for G samples while a more pronounced and continuous exposure is seen for AS and P ones. Aiming to understand the role played by the grinding-induced compressive residual stresses, the study is extended to coated systems where ground substrates are thermal annealed (for relieving stresses) before being ion etched and coated. It yielded lower critical loads and changes in the mechanisms for the scratch-related failure; the latter depending on the relative orientation between scratching and grinding directions. |
dc.format.extent | 11 p. |
dc.language.iso | eng |
dc.publisher | Elsevier |
dc.rights.uri | http://creativecommons.org/licenses/by-nc-nd/3.0/es/ |
dc.subject | Àrees temàtiques de la UPC::Enginyeria dels materials |
dc.subject.other | Coated hardmetal |
dc.subject.other | Grinding |
dc.subject.other | Scratch failure mechanisms |
dc.subject.other | Scratch resistance |
dc.subject.other | Substrate surface finish |
dc.title | Substrate surface finish effects on scratch resistance and failure mechanisms of TiN-coated hardmetals |
dc.type | Article |
dc.subject.lemac | Materials -- Propietats mecàniques |
dc.contributor.group | Universitat Politècnica de Catalunya. CIEFMA - Centre d'Integritat Estructural, Fiabilitat i Micromecànica dels Materials |
dc.identifier.doi | 10.1016/j.surfcoat.2015.01.038 |
dc.description.peerreviewed | Peer Reviewed |
dc.relation.publisherversion | http://www.sciencedirect.com/science/article/pii/S0257897215000729 |
dc.rights.access | Open Access |
local.identifier.drac | 15623858 |
dc.description.version | Postprint (author's final draft) |
local.citation.author | Yang, J.; Roa, J.J.; Oden, M.; Johansson, M.; Esteve, J.; Llanes, L. |
local.citation.publicationName | Surface and coatings technology |
local.citation.volume | 265 |
local.citation.startingPage | 174 |
local.citation.endingPage | 184 |
Fitxers d'aquest items
Aquest ítem apareix a les col·leccions següents
-
Articles de revista [960]
-
Articles de revista [283]