Free-standing flexible magnetoelectric 0–3 composite films comprising CoFe2O4 non-spherical ferromagnetic nanoparticles with strong magnetic anisotropy in soft polyvinylidene fluoride matrices with significant void ratios have been prepared at low temperatures by solvent casting, melt crystallization and mechanical stretching. Magnetoelectric voltage coefficients increase linearly with applied dc magnetic field bias up to 5 kOe. At this field, a maximum magnetoelectric voltage coef¿cient of 11.2 mV cm-1 Oe-1 was obtained for samples with 10 wt% ferrite at *50-kHz resonance. The observed linear magnetoelectric response is attributed to a linear gradient of magnetostriction with respect to magnetic field for H B 5 kOe.
CitationMartins, P. [et al.]. Large linear anhysteretic magnetoelectric voltage coeficients in CoFe2O4/polyvinylidene ¿uoride 0–3 nanocomposites. "Journal of nanoparticle research", 06 Juliol 2013, vol. 15, núm. 1825, p. 1-6.
All rights reserved. This work is protected by the corresponding intellectual and industrial property rights. Without prejudice to any existing legal exemptions, reproduction, distribution, public communication or transformation of this work are prohibited without permission of the copyright holder. If you wish to make any use of the work not provided for in the law, please contact: email@example.com