Slow ß relaxation in La-based metallic glasses based on mechanical spectroscopy measurements
10.1016/S1006-706X(17)30059-6
Inclou dades d'ús des de 2022
Cita com:
hdl:2117/108596
Tipus de documentArticle
Data publicació2017-04-01
Condicions d'accésAccés obert
Llevat que s'hi indiqui el contrari, els
continguts d'aquesta obra estan subjectes a la llicència de Creative Commons
:
Reconeixement-NoComercial-SenseObraDerivada 3.0 Espanya
Abstract
Dynamic mechanical relaxations of La-based metallic glasses were investigated by mechanical spectroscopy. In the framework of the mixing enthalpy of constituent atoms, it was found that ß relaxation was less evident by the addition of Cu to replace Ni in the LaCuNiAl glassy alloy. By introducing Cu into the LaNiAl metallic glass, the mixing enthalpy was less negative, which led to weaker ß relaxation of the metallic glasses. The a relaxation of the La-based metallic glasses could be described by a Kohlrausch-Williams-Watts (KWW) function with a Kohlrausch exponent ßKWW around 0.5. It should be noted that physical aging above the glass transition temperature Tg induced a decrease of ß relaxation intensity in the La-based metallic glass.
CitacióQiao, J., Pelletier, J., Li, N., Crespo, D., Yao, Y. Slow ß relaxation in La-based metallic glasses based on mechanical spectroscopy measurements. "Journal of iron and steel research international", 1 Abril 2017, vol. 24, núm. 4, p. 1-5.
ISSN1006-706X
Versió de l'editorhttp://www.sciencedirect.com/science/article/pii/S1006706X17300596
Col·leccions
Fitxers | Descripció | Mida | Format | Visualitza |
---|---|---|---|---|
Qiao 2017 Slow ... measurements preprint.pdf | 762,4Kb | Visualitza/Obre |