Residual stresses induced by honing processes on hardened steel cylinders
Visualitza/Obre
Final version.pdf (2,174Mb) (Accés restringit)
Sol·licita una còpia a l'autor
Què és aquest botó?
Aquest botó permet demanar una còpia d'un document restringit a l'autor. Es mostra quan:
- Disposem del correu electrònic de l'autor
- El document té una mida inferior a 20 Mb
- Es tracta d'un document d'accés restringit per decisió de l'autor o d'un document d'accés restringit per política de l'editorial
Cita com:
hdl:2117/100210
Tipus de documentArticle
Data publicació2016-06-01
Condicions d'accésAccés restringit per política de l'editorial
Llevat que s'hi indiqui el contrari, els
continguts d'aquesta obra estan subjectes a la llicència de Creative Commons
:
Reconeixement-NoComercial-SenseObraDerivada 3.0 Espanya
Abstract
In the present paper, residual stresses induced by honing processes on hardened steel cylinders were determined. Cubic boron nitride (CBN) abrasives were employed. Both surface measurements and depth profiles were obtained by means of XRD. SEM observations were performed on samples’ surface. Roughness and material removal rate were also measured. Compressive residual stresses, which are known to increase fatigue life of components, were reported both in the axial and in the tangential direction. Shearing stresses were negligible. If only rough honing is taken into account, as a general trend, the lower cutting conditions used, the higher surface stresses are. A similar situation was found when only semifinish or only finish honing is considered. In most cases studied, stress profiles similar to those obtained in grinding processes, in which compressive stresses decrease with depth, were observed. However, in rough honing at hard cutting conditions, a typical hook-shaped profile was found with maximum compressive stress at 80-µm depth. Such shape is usual in turning processes. In order to obtain high surface stresses a rough, semifinish or finish honing operation with low cutting conditions is recommended. However, if stresses are to be obtained at a certain depth, rough honing at high cutting conditions is to be selected.
CitacióBuj, I., Vivancos, J., Setien, I., San Sebastian, M. Residual stresses induced by honing processes on hardened steel cylinders. "International journal of advanced manufacturing technology", 1 Juny 2016.
ISSN0268-3768
Versió de l'editorhttp://link.springer.com/article/10.1007%2Fs00170-016-8870-3
Fitxers | Descripció | Mida | Format | Visualitza |
---|---|---|---|---|
Final version.pdf | 2,174Mb | Accés restringit |