Títol: The effect of anionic clay particles on the structure and thermomechanical behavior of sodium partially-neutralized EMAA ionomer
Autor: Ardanuy Raso, Mònica Veure Producció científica UPC; Velasco Perero, José Ignacio Veure Producció científica UPC; Rodríguez-Pérez, Miguel Ángel; Saja, José Antonio de
Data: 20-jun-2010
Tipus de document: Article
Resum: Nanocomposites based on a sodium partially-neutralized ionomer of poly (ethylene-comethacrylic acid) (EMAA) and MgAl layered double hydroxide (LDH) particles with and without organic modification were prepared from a melt mixing process. The structure was characterized using X-ray diffraction analysis (XRD) and transmission electron microscopy (TEM). Although TEM micrographies revealed the presence of agglomerates of LDH sheets, the achievement of an exfoliated structure was observed when dodecyl sulphate-modified LDH particles were used. The effects of the LDH particles on the thermomechanical properties of EMAA were analyzed using differential scanning calorimetry (DSC) and dynamic mechanical thermal analysis (DMTA). The thermal transition of the ionic aggregates and dynamic mechanical response of EMAA were found strongly modified by these particles, resulting in an increase on the storage modulus and a decrease on the loss factor values. Moreover, the alpha relaxation of the composites was visibly shifted to higher temperatures
Descripció: Electronic version of an article published as "Journal of Applied Polymer Science", Vol. 116, issue 5, p.2573–2579 (2010)
ISSN: 0021-8995
URI: http://hdl.handle.net/2117/6613
DOI: 10.1002/app.31818
Versió de l'editor: http://www3.interscience.wiley.com/cgi-bin/fulltext/123243940/PDFSTART
Apareix a les col·leccions:POLYCOM - Polimers i compòsits: tecnologia. Articles de revista
Departament d'Enginyeria Tèxtil i Paperera. Articles de revista
Departament de Ciència dels Materials i Enginyeria Metal·lúrgica. Articles de revista
Altres. Enviament des de DRAC
Comparteix:


Stats Mostra les estadístiques d'aquest ítem

SFX Query

Aquest ítem (excepte textos i imatges no creats per l'autor) està subjecte a una llicència de Creative Commons Llicència Creative Commons
Creative Commons

 

Valid XHTML 1.0! Programari DSpace Copyright © 2002-2004 MIT and Hewlett-Packard Comentaris
Universitat Politècnica de Catalunya. Servei de Biblioteques, Publicacions i Arxius