Citació: Lavilla, C. [et al.]. Bio-based poly(butylene terephthalate) copolyesters containing bicyclic diacetalized galactitol and galactaric acid: Influence of composition on properties. "Polymer", 19 Juliol 2012, vol. 53, núm. 16, p. 3432-3445.
Títol: Bio-based poly(butylene terephthalate) copolyesters containing bicyclic diacetalized galactitol and galactaric acid: Influence of composition on properties
Autor: Lavilla Aguilar, Cristina Veure Producció científica UPC; Alla Bedahnane, Abdelilah Veure Producció científica UPC; Martínez de Ilarduya Sáez de Asteasu, Domingo Antxon Veure Producció científica UPC; Benito, Elena; García Martín, Maria de Gracia; Galbis Pérez, Juan Antonio; Muñoz Guerra, Sebastián Veure Producció científica UPC
Editorial: Elsevier
Data: 19-jul-2012
Tipus de document: Article
Resum: Copolyesters from 1,4-butanediol, dimethyl terephthalate and either 2,3:4,5-di-O-methylene-galactitol or dimethyl 2,3:4,5-di-O-methylene-galactarate with compositions of 10, 20, 30, 40 and 50% of either galactitol or galactarate units were prepared by melt-polycondensation. The copolyesters had Mw in the 32,000–41,000 g mol−1 range and had a random microstructure. They displayed Tg from 20 to 70 °C with values steadily decreasing with the content in galactarate units but increasing with the content in galactitol units. All the copolyesters were semicrystalline with Tm between 115 and 210 °C and they adopted the crystal structure of PBT. Copolyesters containing up to 20% of galactitol units as well as all galactarate copolyesters were able to crystallize from the melt, at a crystallization rate that decreased with the content in carbohydrate-based units. Stress-strain essays revealed an increment in the tensile strength and elastic modulus with increasing contents in galactitol units whereas these parameters decreased when galactarate units were the replacing ones.
ISSN: 0032-3861
URI: http://hdl.handle.net/2117/16817
DOI: dx.doi.org/10.1016/j.polymer.2012.05.048
Versió de l'editor: http://www.sciencedirect.com/science/article/pii/S0032386112004648
Apareix a les col·leccions:Altres. Enviament des de DRAC
POL - Polímers. Articles de revista
Departament d'Enginyeria Química. Articles de revista
Comparteix:


Stats Mostra les estadístiques d'aquest ítem

SFX Query

Aquest ítem (excepte textos i imatges no creats per l'autor) està subjecte a una llicència de Creative Commons Llicència Creative Commons
Creative Commons

 

Valid XHTML 1.0! Programari DSpace Copyright © 2002-2004 MIT and Hewlett-Packard Comentaris
Universitat Politècnica de Catalunya. Servei de Biblioteques, Publicacions i Arxius