Citació: Roman, F. [et al.]. Identification of nanostructural development in epoxy polymer layered silicate nanocomposites from the interpretation of differential scanning calorimetry and dielectric spectroscopy. "Thermochimica acta", 08 Maig 2012, núm. 541, p. 76-85.
Títol: Identification of nanostructural development in epoxy polymer layered silicate nanocomposites from the interpretation of differential scanning calorimetry and dielectric spectroscopy
Autor: Román Concha, Frida Rosario Veure Producció científica UPC; Calventus Solé, Yolanda Veure Producció científica UPC; Colomer Vilanova, Pere Veure Producció científica UPC; Hutchinson, John M. Veure Producció científica UPC
Data: 8-mai-2012
Tipus de document: Article
Resum: The effect of nanoclay on the non-isothermal cure kinetics of polymer layered silicate nanocomposites based upon epoxy resin is studied by calorimetric techniques (DSC and TGA) and by dielectric relaxation spectroscopy (DRS) in non-isothermal cure at constant heating rate. The cure process takes place by homopolymerisation, initiated anionically using 3 wt% dimethylaminopyridine (DMAP), and the influence of the nanoclay content has been analysed. Interesting differences are observed between the nanocomposites with 2 wt% and 5 wt% clay content. At low heating rates, these samples vitrify and then devitrify during the cure. For the sample with 2 wt% clay, the devitrification is accompanied by a thermally initiated homopolymerisation, which can be identified by DRS but not by DSC. The effect of this is to improve the exfoliation of the nanocomposite with 2 wt% clay, as verified by transmission electron microscopy, with a corresponding increase in the glass transition temperature. These observations are interpreted in respect of the nanocomposite preparation method and the cure kinetics.
ISSN: 0040-6031
URI: http://hdl.handle.net/2117/16040
DOI: 10.1016/j.tca.2012.05.001
Versió de l'editor: http://www.sciencedirect.com/science/article/pii/S0040603112002079
Apareix a les col·leccions:Altres. Enviament des de DRAC
TERFIQ - Grup de Termodinàmica i Fisico-Química. Articles de revista
Departament de Màquines i Motors Tèrmics. Articles de revista
Comparteix:


Stats Mostra les estadístiques d'aquest ítem

SFX Query

Aquest ítem (excepte textos i imatges no creats per l'autor) està subjecte a una llicència de Creative Commons Llicència Creative Commons
Creative Commons

 

Valid XHTML 1.0! Programari DSpace Copyright © 2002-2004 MIT and Hewlett-Packard Comentaris
Universitat Politècnica de Catalunya. Servei de Biblioteques, Publicacions i Arxius