Citació: Abalos, C. [et al.]. Influence of topographical feature on the fluoride corrosión of Ni-Ti orthodontic archwires. "Journal of Materials Science: Materials in Medicine", 2011, núm. 22, p. 2813-2821.
Títol: Influence of topographical feature on the fluoride corrosión of Ni-Ti orthodontic archwires
Autor: Abalos, C.; Paúl, A.; Mendoza, A.; Solano, E.; Gil Mur, Francisco Javier Veure Producció científica UPC
Editorial: Springer
Data: 2011
Tipus de document: Article
Resum: Different manufacturing processes of Ni–Ti archwires respond differently to corrosion due to the surface conditions involved. In this study, several topographical features and their influence upon fluoride corrosion were studied. Four topographies (smooth, dimple, scratch, and crack) according to the main surface defect were characterized (n = 40). Static corrosion tests were performed in artificial saliva with fluorated prophylactic gel (12500 ppm) for 28 days. The surface was characterized by SEM and laser confocal microscopy. Standard electrochemical corrosion (open circuit potential, corrosion potential and corrosion current density) was performed. Statistical analysis was carried out using the ANOVA test (a B 0.05). An increase was observed in the surface defects and/or roughness of the cracked and scratched surfaces. These defects produced an important increase in corrosion behavior. The best surfaces for the orthodontic archwires were the smooth and dimpled surfaces, respectively. The increase in defects was independent of roughness. Manufacturing processes that produce surface cracks should be avoided in orthodontic applications.
ISSN: 1573-4838
URI: http://hdl.handle.net/2117/15162
DOI: 10.1007/s10856-011-4460-y
Apareix a les col·leccions:Altres. Enviament des de DRAC
BIBITE - Biomaterials, Biomecànica i Enginyeria de Teixits. Articles de revista
Departament de Ciència dels Materials i Enginyeria Metal·lúrgica. Articles de revista

Stats Mostra les estadístiques d'aquest ítem

SFX Query

Aquest ítem (excepte textos i imatges no creats per l'autor) està subjecte a una llicència de Creative Commons Llicència Creative Commons
Creative Commons


Valid XHTML 1.0! Programari DSpace Copyright © 2002-2004 MIT and Hewlett-Packard Comentaris
Universitat Politècnica de Catalunya. Servei de Biblioteques, Publicacions i Arxius