Citació: Pavon, J. [et al.]. Anodic oxidation of titanium for implants and prothesis: processing characterization and potential improvement of osteointegration. A: Congreso Latinoamericano de Ingeniería Biomédica. "Actas CLAIB 2011". La Habana: 2011, p. 1-4.
Títol: Anodic oxidation of titanium for implants and prothesis: processing characterization and potential improvement of osteointegration
Autor: Anglada Gomila, Marcos Juan Veure Producció científica UPC; Pavon, Juan José; Galvis, Oscar; Echevarria, F; Castaño, J; Echeverry, M; Robledo, S; Jiménez Piqué, Emilio Veure Producció científica UPC; Mestra Rodríguez, Álvaro Miguel Veure Producció científica UPC
Data: 2011
Tipus de document: Conference report
Resum: Among all biomaterials used for bone replacement, it is recognized that both commercially pure titanium (Ti c.p.) and Ti6Al4V alloy are the materials that show the best in vivo performance due to their excellent balance between mechanical, physical-chemical and biofunctional properties. However, one of its main drawbacks, which compromise the service reliability of the implants and its osteointegration capacity, is the thin film of fibrous tissue around the implant due to the bioinert behaviour of titanium. One of the alternatives more studied to improve the titanium osteointegration is the surface modification through the control of the roughness parameters within a specific range which is recognized that improve the osteoblasts adhesion. In this work is investigated the influence of different electrochemical processing conditions for surface modification of c.p. Ti, in their microstructural, morphological, topographical and mechanical properties, as well as in their biological behaviour. The electrochemical anodizing treatment was performed by using different electrolytes based on phosphoric acid (H3PO4), sulphuric acid (H2SO4) with a fluoride salt; and the Focused Ion Beam (FIB) technique, normally named as Nanolab, was used for the microstructural, chemical and morphological characterization, as well as the confocal laser microscopy technique which also served for roughness measurements. The mechanical response of the anodic layers was evaluated through the using of a scratch tester which showed the critical loads for the coating damages. The characterization results showed that both, concentrations and electrolyte species, clearly influenced the morphological and topographical features, as well as the chemical composition of the anodic layer. By using the FIB was possible to detect nanopores within both the surface and the bulk of the coating. Some of the conditions generated a very special coating morphology which promoted a better osteoblasts adhesion. Contrary to what it was a priory expected, all anodic coatings showed high critical loads for damages during scratch test, despite their high porosity, which could be related with some defects coalescence mechanism that allows dissipating the high stress concentration applied during the test.
URI: http://hdl.handle.net/2117/14906
Apareix a les col·leccions:Altres. Enviament des de DRAC
CIEFMA - Centre d'Integritat Estructural i Fiabilitat dels Materials. Ponències/Comunicacions de congressos
Departament de Ciència dels Materials i Enginyeria Metal·lúrgica. Ponències/Comunicacions de congressos
Comparteix:


Stats Mostra les estadístiques d'aquest ítem

SFX Query

Aquest ítem (excepte textos i imatges no creats per l'autor) està subjecte a una llicència de Creative Commons Llicència Creative Commons
Creative Commons

 

Valid XHTML 1.0! Programari DSpace Copyright © 2002-2004 MIT and Hewlett-Packard Comentaris
Universitat Politècnica de Catalunya. Servei de Biblioteques, Publicacions i Arxius