Citació: Mejía, I. [et al.]. Determination of the critical conditions for the initiation of dynamic recrystallization in boron microalloyed steels. "Materials science and engineering A. Structural materials properties microstructure and processing", 15 Maig 2011, vol. 528, núm. 12, p. 4133-4140.
Títol: Determination of the critical conditions for the initiation of dynamic recrystallization in boron microalloyed steels
Autor: Mejía, Ignacio; Bedolla Jacuinde, Arnoldo; Maldonado, Cuauhtémoc; Cabrera Marrero, José M. Veure Producció científica UPC
Data: 15-mai-2011
Tipus de document: Article
Resum: From the present research, the critical conditions associated with the onset of dynamic recrystallization (DRX) of hot deformed boron microalloyed steels were precisely determined based on changes in the strain hardening rate ( ) as a function of the flow stress. For this purpose, a low carbon steel microalloyed with four different amounts of boron (29, 49, 62 and 105 ppm) was deformed by uniaxial hot-compression tests at high temperature (950, 1000, 1050 and 1100 ◦C) and constant true strain rate (10−3, 10−2 and 10−1 s−1). Results indicate that the critical conditions for the initiation of dynamic recrystallization depend on the temperature and strain rate. In addition, both critical stress c, and critical strain εc, were noticed to decrease as boron content increased. Such a behavior is attributed to a solute drag effect by boron atoms on the austenitic grain boundaries and also to a solid solution softening effect. The critical ratios c/ p and εc/εp for all boron microalloyed steels remain fairly constant (≈0.82 and ≈0.53, respectively), such values are in agreement with those commonly reported for Al-killed, C–Mn, Nb, Nb–Ti, high carbon and stainless steels.
ISSN: 0921-5093
URI: http://hdl.handle.net/2117/12649
DOI: 10.1016/j.msea.2011.01.102
Versió de l'editor: linkinghub.elsevier.com/retrieve/pii/S0921509311001249
Apareix a les col·leccions:Altres. Enviament des de DRAC
PROCOMAME - Processos de Conformació de Materials Metàl·lics. Articles de revista
Departament de Ciència dels Materials i Enginyeria Metal·lúrgica. Articles de revista
Comparteix:


Stats Mostra les estadístiques d'aquest ítem

SFX Query

Aquest ítem (excepte textos i imatges no creats per l'autor) està subjecte a una llicència de Creative Commons Llicència Creative Commons
Creative Commons

 

Valid XHTML 1.0! Programari DSpace Copyright © 2002-2004 MIT and Hewlett-Packard Comentaris
Universitat Politècnica de Catalunya. Servei de Biblioteques, Publicacions i Arxius