Citació: Calvo, J. [et al.]. Influence of the chemical composition on transformation behaviour of low carbon microalloyed steels. "Materials science and engineering A. Structural materials properties microstructure and processing", 2009, vol. 520, núm. 1-2, p. 90-96.
Títol: Influence of the chemical composition on transformation behaviour of low carbon microalloyed steels
Autor: Calvo Muñoz, Jessica Veure Producció científica UPC; Hung, I. H.; Elwazri, A. M.; Bai, D.; Yue, S.
Data: 2009
Tipus de document: Article
Resum: In order to design thermomechanical schedules for processing lowcarbon microalloyed steels, the various critical transformation temperatures, i.e. the start and finish of the austenite transformation (Ar3, Ar1) and the non-recrystallization temperature (Tnr), must be determined. Continuous cooling torsion and compression testing are useful ways to measure these values. In this study six low carbon microalloyed steels with different additions (Nb, Cu, Si and Mo) were examined using these techniques. Moreover, the equilibrium phase diagrams for each alloy were calculated using FactSage. The comparison of the thermomechanical testing results with the thermodynamic calculations leads to a better understanding of the effect of the different elements on the transformation behaviour of pipeline steels. Regarding transformation temperatures, Cu in residual contents showed a strong effect on decreasing both Ar3 and Ar1, which indicates a hardenability effect of this element. On the other hand, increasing Nb contents increased Tnr by accelerating Nb(C,N) precipitation. However, when Si was added to a Nb-microalloyed steel, the Tnr decreased.
ISSN: 0921-5093
URI: http://hdl.handle.net/2117/11990
DOI: 10.1016/j.msea.2009.05.027
Apareix a les col·leccions:Altres. Enviament des de DRAC
PROCOMAME - Processos de Conformació de Materials Metàl·lics. Articles de revista
Departament de Ciència dels Materials i Enginyeria Metal·lúrgica. Articles de revista
Comparteix:


Stats Mostra les estadístiques d'aquest ítem

SFX Query

Aquest ítem (excepte textos i imatges no creats per l'autor) està subjecte a una llicència de Creative Commons Llicència Creative Commons
Creative Commons

 

Valid XHTML 1.0! Programari DSpace Copyright © 2002-2004 MIT and Hewlett-Packard Comentaris
Universitat Politècnica de Catalunya. Servei de Biblioteques, Publicacions i Arxius