Citació: Franco, M.; Rodriguez, R.; Puiggali, J. Influence of degradation on the crystallization behaviour of a biodegradable segmented copolymer constituted by glycolide and trimethylene carbonate units. "Polymer degradation and stability", Desembre 2010, vol. 95, núm. 12, p. 2376-2387.
Títol: Influence of degradation on the crystallization behaviour of a biodegradable segmented copolymer constituted by glycolide and trimethylene carbonate units
Autor: Franco García, María Lourdes Veure Producció científica UPC; Rodríguez Galán, Rafael Alfonso Veure Producció científica UPC; Puiggalí Bellalta, Jordi Veure Producció científica UPC
Data: des-2010
Tipus de document: Article
Resum: The influence of degradation on non-isothermal crystallization from the melt of a segmented copolymer constituted of glycolide and trimethylene carbonate units and used as a bioabsorbable surgical suture was studied by optical microscopy, differential scanning calorimetry and time-resolved X-ray diffraction. Fibrillar positive spherulites were obtained with slightly degraded samples but new axialitic morphologies were detected when samples had a molecular weight, Mw, lower than 29,000 g/mol and the crystallization started at a high temperature. Crystal growth kinetics of samples degraded under different conditions was evaluated over a wide temperature range by a non-isothermal method. Two crystallization regimes (I and II) were determined for the more degraded samples (i.e., those able to crystallize according to axialitic and spherulitic morphologies), whereas only regime II was found for samples of higher molecular weights. Primary nucleation density decreased with the extent of degradation provided no morphological changes occurred, and so did the regularity of lamellar stacking, as shown by synchrotron measurements, although the morphological parameters remained practically constant.
ISSN: 0141-3910
URI: http://hdl.handle.net/2117/11660
Apareix a les col·leccions:PSEP - Polimers Sintètics: Estructura i Propietats. Polimers Biodegradables.. Articles de revista
Departament d'Enginyeria Química. Articles de revista
Altres. Enviament des de DRAC
Comparteix:


Stats Mostra les estadístiques d'aquest ítem

SFX Query

Aquest ítem (excepte textos i imatges no creats per l'autor) està subjecte a una llicència de Creative Commons Llicència Creative Commons
Creative Commons

 

Valid XHTML 1.0! Programari DSpace Copyright © 2002-2004 MIT and Hewlett-Packard Comentaris
Universitat Politècnica de Catalunya. Servei de Biblioteques, Publicacions i Arxius